Bullet-proof and stab-proof clothing

1. APPEARANCE: bullet-proof stab-proof clothing consists of jacket and protective layer (including protective layer) . (if the jacket is covered with other materials, the material should be removed before the performance test. If not removed, the material should be used as part of the protective layer to evaluate the structure, weight, thickness and area.). Detachable washing jacket, shoulder, waist size can be adjusted. All Materials of the protective layer have the same size and specification, and the surface of the material has no defects such as hole, deep hole, scratch, crack notch, corner Burr, etc. . Coat and protective layer size should match, protective layer should be firmly connected with the coat with light-proof, waterproof black protective cover sealing, uniform sealing edge. The protective sleeve material should have anti-seepage performance, anti-hydrostatic pressure should be greater than or equal to 18 KPA. The jacket and the protective layer should match each other, and the protective layer should be firmly connected with the jacket. Bullet-proof and stab-proof clothing should have good air permeability and be easy to wear off. After wearing, it should not restrict the free movement of two arms and human body kneeling, prostrating, jumping, squatting, running, pitching, turning and so on. 2. Protective Area: the protective layer should cover the main internal organs of the human body (including front, back and side protection) . The total area of the protective layer is 0.3 m23. The thickness of the protective layer is 16.5 MM4. The weight of the protective layer is 3.5 kg，5. bullet-proof performance: At normal temperature: under normal temperature, the sample is fired at a distance of 5m with a 79 type 7.62 mm light submachine gun and a 51 type 7.62 mm pistol bullet (lead core) , and the sample is not penetrated, the depth of the depression formed on the backing material is not more than 25 mm at high temperature: After the high temperature test (55 °C ± 2 °C, constant temperature 4h) , the samples are shot at a distance of 5 m within 15 minutes, and the samples are not penetrated; The depth of the depression formed on the backing material is not more than 25mm at low temperature: After the low temperature (- 20 °C ± 2 °C, constant temperature 4h) , the samples were shot at a distance of 5m within 15Min, and the samples were not penetrated; The depth of the depression formed on the backing material is not more than 25 mm. The sample is immersed in 0.5 m deep water at room temperature, left to rest for 30 minutes, and then dropped for 5 minutes. The sample is shot at 5 m distance The depth of the depression formed on the backing material is not more than 25mm wet heat: After the wet heat (70 °C ± 2 °C, 80% rh constant temperature and humidity 240h) test, the sample is placed at room temperature for 24h, and the sample is shot at a distance of 5M, the sample is not penetrated; The depth of recesses formed in the backing material shall not be greater than 25 mm，6、 stab-proof performance test: At normal temperature: at normal temperature, 2.4 kg of falling body was formed by Standard Test Tool plus weight, 24 j ± 0.5 j impact energy was used, and the sample was punctured effectively at 0,45 ° penetration angle, the point of the knife is not allowed to penetrate the sample at high temperature: After being treated at high temperature (55 °C ± 2 °C, constant temperature 4 h) , the falling body is composed of 2.4 kg with standard test tools and a weight of 24 j ± 0.5 j impinging energy, the sample is effectively impaled at the penetration angle of 0 and 45 ° , the cutting point is not allowed to penetrate into the sample at low temperature: After low temperature (- 20 °C ± 2 °C, constant temperature 4 h) , the falling body is reconstituted by standard test cutting tools and the impact energy is 24 j ± 0.5 j, and the sample is effectively impaled at the penetration angle of 0,45 ° , the knife point is not allowed to penetrate the sample 9, the Implementation Standard: meets “GA 141-2010 police body armor”, “Ga 68-2008 police body armor”standard; I provide national security alarm system product Quality Supervision and Inspection Center (Beijing) Ministry of Public Security and Police Electronic Product Quality Inspection Center issued by the test report.

Product process and material: the protective layer structure from the impact surface is successively: 6 layers of Arlene woven fabric, 23 layers of high-performance polyethylene weft free cloth (4 layers of fiber orthogonal), 4 layers of Arlene woven fabric, 6MM thick foam sheet.

Colors and styles can be customized